Impact and wear resistant material for armored chassis (SG D409)
Applied to metal parts, hardware objects collide with each other, and can prevent hail damage and other occasions, such as armored vehicle chassis, assault boat, fender, buoy, ship deck, bunker funnel, vehicle collision layer, concrete mixing tower, conveyor belt, large warehouse, can also be widely used in aviation, aerospace, construction, military and other fields.
keyword：system
Category:
Coatings (including special coatings)
Message
Product description
| Item | Performance index |
| Gel time (S) | 11 |
| Tensile strength (MPa) | ≥25 |
| Fracture elongation rate (%) | ≥400 |
| Tear strength (N/mm) | ≥70 |
| Hardness (Shao A) | ≥85 |
| Impact resistance/(drop hammer height 100cm) | No cracks, wrinkles, no peeling |
| Drying time (25±2℃) | The surface is dry within 1 minute, and the walking intensity can be reached in 10 minutes |
| Friction coefficient | 0.75-0.85 |
| Wear resistance /(Akron method, cm3/1.61km) | ≤0.36 |
| Adhesion (Metal substrate, pulling method, MPa) | ≥5.5 |
| Resistant medium /168h | No rust, no foaming, no shedding |
| Colour | Can be modulated according to user requirements |
Note: The above parameters can be sprayed with GRACOH-X3 host and AP spray gun under laboratory conditions and tested for physical properties after curing at room temperature for 7 days. Due to differences in site conditions, the actual measured data on site may differ from the above data.